Metal injection molded base for a data storage system

ABSTRACT

The present invention provides a data storage system. The data storage system includes a metal injected molded base. The metal injection molded base includes a metal injection molded platform and at least one metal injection molded three-dimensional feature. The at least one metal injection molded three-dimensional feature is formed integrally and simultaneously with the metal injection molded platform. The at least one three-dimensional feature configured to mount data storage system components to the platform.

FIELD OF THE INVENTION

The present invention relates generally to data storage systems. Inparticular, the present invention relates to a base for a data storagesystem.

BACKGROUND OF THE INVENTION

Disc drives are typical data storage systems. A disc drive includes arigid housing having a base and a cover that encloses a variety ofcomponents. The components include one or more discs having datasurfaces that are coated with a magnetizable medium for storage ofdigital information in a plurality of circular, concentric data tracks.The discs are mounted on a spindle motor that causes the discs to spinand the data surfaces of the discs to pass under respective aerodynamicbearing disc head sliders. The sliders carry magnetic transducers, whichwrite information to and read information from the data surfaces of thediscs.

The components also include an actuator mechanism that moves the slidersacross the data surfaces of the discs. The actuator mechanism includes amotor, such as a voice coil motor (VCM), a track accessing arm andsuspensions that support the sliders. The voice coil motor is operatedso as to move the actuator mechanism about an actuator pivot center suchthat the sliders move from track-to-track across the data surface of adisc.

The base of the disc drive is a complex three-dimensional structure thattypically provides a rigid and precise platform upon which multiplemechanical and electronic components, as discussed above, are mounted.Typically, small form factor disc drives include a base made of stampedsteel. A stamped steel base can be cost effective and includes a highstrength. Stamped steel bases, however, have many limitations. It isdifficult to achieve variations in thickness at different portions ofthe base as well as it being practically impossible to achieve smallcorner radiuses without machining the base after it has been stamped. Infact, a stamped base design includes through holes where high thicknessvariation ratios are required. The existence of through holes introducesadditional sealing costs and potential leakage problems.

A base includes a variety features for various applications of a discdrive that can not be achieved through pure stamping technology.Typically, force fit components are coupled to a stamped base to satisfythese disc drive application needs. However, forming suitable threads inthe base for use in receiving force fit components is difficult.Imperfectly formed threads cause potential leakage problems, corrosionissues on the interface and possible loose fittings between the base andthe force fit components. Many times features that should be mounted tothe base (such as the breather filter support, carbon filter support,latches, crash stop and etc) are mounted to the top cover to mitigatemany of the problems associated with the stamping process. However,mounting such features to the top cover introduces additional disc drivedimensional problems.

The above-mentioned problems associated with stamped steel bases havenot posed problems for large disc drives. Normally, large disc drivesare made from an aluminum die casting process. However, an aluminum diecast base for small form factor disc drives is not an ideal design forperformance and cost reasons. Examples of problems for an aluminum diecast base include low material stiffness and the lack of magneticproperties.

Embodiments of the present invention provide solutions to these andother problems, and offer other advantages over the prior art.

SUMMARY OF THE INVENTION

The present invention provides a data storage system. The data storagesystem includes a metal injected molded base. The metal injection moldedbase includes a metal injection molded platform and at least one metalinjection molded three-dimensional feature. The at least onethree-dimensional features is formed integrally and simultaneously withthe platform.

One of the three-dimensional features is a metal injection molded motorhousing. The motor housing is formed integrally and simultaneously withthe injection molded platform. The motor housing is configured to housea motor that rotates a medium about an axis.

The present invention also provides a method for forming an injectionmolded base of a data storage system. The method includes mixing a metalpowder with a polymer binding material. The mixture is injected into amold to provide the base. The mold is adapted to form a platform andadapted to form three-dimensional features that are integral with theplatform. The mold is heated in an oven for de-bonding and the mold isheated in an oven for sintering.

Other features and benefits that characterize embodiments of the presentinvention will be apparent upon reading the following detaileddescription and review of the associated drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a simplified schematic diagram of a data storagesystem.

FIG. 2 illustrates a top perspective view of force fit componentsexploded from a stamped base of a data storage system.

FIG. 3 illustrates a top perspective view of force fit componentsassembled to a stamped base of a data storage system.

FIG. 4 illustrates a bottom perspective view of force fit componentsassembled to a stamped base of a data storage system.

FIG. 5 illustrates a top perspective view of a metal injection moldedbase of a data storage system.

FIG. 6 illustrates a bottom perspective view of a metal injection moldedbase of a data storage system.

FIG. 7 is a flowchart illustrating a process of forming a metalinjection molded base.

DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

FIG. 1 is a simplified schematic diagram of a disc drive 100 in whichembodiments of the present invention are useful. Disc drives are commondata storage systems. Disc drive 100 includes an enclosure 101.Enclosure 101 includes a base (not shown in FIG. 1) and a top cover (notshown). Disc drive 100 includes a disc 107. Those skilled in the artshould recognize that disc drive 100 can contain a single disc, asillustrated in FIG. 1, or multiple discs included in a disc pack. Asillustrated in FIG. 1, disc 107 is mounted on a spindle motor 105 forrotation about central axis 109. Each disc surface has an associatedslider 110, which carries a read/write head for communication with thesurface of the disc.

Each slider 110 is supported by a suspension 112 which is in turnattached to a track accessing arm 114 of an actuator mechanism 116.Actuator mechanism 116 is rotated about a shaft by a voice coil 134 of avoice coil motor 118. As voice coil motor 118 rotates actuator mechanism116, slider 110 moves in an arcuate path 122 between a disc innerdiameter 124 and a disc outer diameter 126. While FIG. 1 illustrates onemanner of actuating a data head proximate a data storage medium, thepresent invention, however, is applicable to data storage systems thatuse other techniques.

Disc drive 100 also includes a printed circuit board (PCB) 136. PCB 136is located outside enclosure 101. In general, PCB 136 is mounted to anouter surface of a base of enclosure 101. PCB 136 supports a pluralityof printed circuit board components (not shown in FIG. 1). The printedcircuit board components are configured to couple to components enclosedwithin enclosure 101, such as spindle motor 105, slider 110, actuatormechanism 116 and voice coil motor 118.

Typically, a base of a small form factor disc drive is formed bystamping steel. A stamped steel base of a small form factor disc driveinclude many advantages, such as cost effectiveness, high materialstrength and the demonstration of magnetic properties. The magneticproperties of the stamped steel base allow the formation of a portion ofa magnetic loop of a voice coil motor, such as voice coil motor 118 ofFIG. 1, or a spindle motor, such as spindle motor 105 of FIG. 1.However, a stamped base of a small form factor disc drive also includessome limitations. For example, it is difficult to achieve variations inthickness at different portions of the stamped base. This examplelimitation consequently results in the need to use force fit componentsthat couple to the stamped base of a small form factor disc drive tosatisfy different disc drive application needs. In addition, thisexample limitation consequently results in the inclusion of throughholes where high thickness variation ratios are required.

FIG. 2 illustrates a top perspective view of an example plurality offorce fit components 204 exploded from an example stamped base 202 of adisc drive. FIG. 3 illustrates a bottom perspective view of the examplestamped base 202. Base 202, illustrated in FIGS. 2 and 3, is stamped toform various surface geometries. Force fit components 204 of base 202are needed to support various elements of data storage system 200 thatcan not be formed with a pure stamping technology. For example, forcefit components 204 include printed circuit board (PCB) screw nuts 206for attaching a printed circuit board (PCB), such as PCB 136 illustratedin FIG. 1, to base 202. Other examples includes a ramp stopper 208, anactuator shaft 210 for supporting an actuator mechanism, such asactuator mechanism 116 illustrated in FIG. 1, and a ramp screw nut 212for attaching a ramp 213 to base 202.

As illustrated in FIG. 2 and more clearly in FIG. 3, stamped base 202 ofdata storage system 200 includes through holes where high thicknessvariation ratios are required. In particular, the stamping technologyrequires that through holes 214 are incorporated into a floor 215 ofmotor housing 216. A high thickness variation is needed to accommodatethe spindle motor stator coils or windings. After the spindle motor isassembled within motor housing 216, through holes 214 located on floor215 need to be sealed. The existence of through holes 214 introducesadditional costs for sealing as well as potential ambient air andhumidity leakage internal to the enclosure of data storage system 200.In addition, through holes 214 cause the local stiffness of motorhousing 216 of base 202 to be low. A lowered stiffness in the spindlemotor housing will limit the external shock that a spindle motor canwithstand and/or introduce vibration and acoustic problems to a datastorage system.

In addition to it being difficult to achieve variations in thickness atdifferent portions of the stamped base, it is also, for allpracticalities, impossible to achieve small corner radiuses withoutmachining the base after it has been stamped. Small corner radiuses helpform proper interfaces between the base and a drive component. Forexample, small corner radiuses of a voice coil motor connector hole 217are desirable for attachment of a voice coil motor. However, performinga second step of machining when forming a base of a small form factordisc drive also contributes to the cost ineffectiveness of the stampedbase.

FIG. 4 illustrates a top perspective view of stamped base 202 afterassembly of the plurality of force fit components 204. In addition tothe above-mentioned limitations, the assembly of force fit components204 to base 202 provides additional limitations. Forming suitablethreads in base 202 for use in receiving force fit components 204 isdifficult. Imperfect threads result in potential leakage problems,corrosion issues and possible loose fittings between force fitcomponents 204 and base 202.

FIG. 5 illustrates a top perspective view of a metal injection molded(MIM) base 302 of a data storage system in accordance with embodimentsof the present invention. MIM base 302 overcomes much of the limitationsof the stamping and aluminum die casting technologies previouslydiscussed as well as retains benefits of each of those technologies. MIMbase 302 can be made of a non-magnetic metal or a magnetic metal.Example non-magnetic metals for MIM base 302 include stainless steel,cold rolled steel, aluminum alloys and other metal alloys. Suchmaterials have a high modulus and, thus, have properties of highstiffness. The content of the material for MIM base 302 can be variedaccording to the needs of a particular drive application. A magnetic MIMbase having high magnetic permeability and low coercivity can form partof the magnetic loop of the voice coil motor and actuator mechanism aswell as part of the magnetic loop for the spindle motor. In particular,MIM base 302 can be a soft magnetic metal such as various permalloys,permendur, 1010 steel, iron and etc. A soft magnetic metal injectionmolded base can help protect a data storage system from externalmagnetic interference.

MIM base 302 includes a metal injection molded (MIM) platform 303 and atleast one metal injection molded (MIM) three-dimensional feature 304.MIM platform 303 and the at least one MIM three-dimensional feature 304forms a single, rigid structure. The at least one MIM three-dimensionalfeature 304 is integrally and simultaneously formed with the MIMplatform 303 to form MIM base 302. Example MIM three-dimensionalfeatures include components that were originally force fit components inthe example stamped base 202 of FIGS. 2 and 3. An example of a moldedand integrally formed features includes PCB screw nuts 306 for attachinga PCB, such as PCB 136 illustrated in FIG. 1, to MIM base 302. Otherexamples include a ramp stopper 308, an actuator shaft 310 forsupporting an actuator mechanism, such as actuator mechanism 116 in FIG.1, and a recirculation filter support 318. Although FIG. 5 illustrates abase 302 having three-dimensional features 304, those skilled in the artshould recognize that other molded three-dimensional features that areformed integrally and simultaneously with MIM platform 303 can be addedto the base without introducing any further costs.

Another example MIM three-dimensional feature includes a motor housing316 illustrated in FIG. 5 and illustrated in the bottom perspective viewof MIM base 302 of FIG. 6. Motor housing 316 is recessed from a topsurface 305 into platform 303. Motor housing 316 is configured to housea spindle motor that rotates a medium about an axis. Although it isshown in FIG. 5, it is more clearly shown in FIG. 6 that motor housing308 includes a continuous and unbroken floor 315. Forming the MIMthree-dimensional floor 315 does not require through holes toaccommodate the high thickness variations needed for providing an areafor the spindle motor stator coils or windings as does the stamped baseshown in the examples illustrated in FIGS. 2-4. Unlike the stamped baseshown in the example illustrated in FIGS. 2-4, the lack of through holeseliminates any potential additional costs for sealing as well aspotential ambient air and humidity leakage internal to the enclosure ofa disc drive. In addition, the lack of through holes causes the localstiffness of motor housing 316 to be higher than that of a stamped motorhousing, such as motor housing 216 illustrated in FIG. 2.

Referring to FIG. 5, the interface between MIM base 302 and a disc drivecomponent mounted to platform 303 is better than the interface between astamped base, such as base 202, and a disc drive component. Cornerradiuses established by metal injection molding are much smaller thanthat of a stamping technology. The smallest corner radius that can beachieved by metal injection molding is almost near zero. However, thesmallest outside bending radius by stamping ranges between 0.3 mm and0.6 mm. For example, small corner radiuses of a voice coil motorconnector hole 317 are desirable for attachment of a voice coil motor.The corner radius of voice coil motor connector hole 317 for MIM base302 is less than 0.1 mm. In comparison, the corner radius of a voicecoil motor connector hole of a stamped base is greater than 0.3 mm. Inaddition, small form factor disc drives desire small corner radiuses dueto the limited space available on the base.

FIG. 7 illustrates a flowchart 400 illustrating several importantprocesses of metal injection molding of a MIM base. At block 402, metalpowder of a select metal or combination of metals is mixed together withpolymer bonding materials. The metal powder of select metal orcombination of metals can be magnetic or non-magnetic. Examples of whichare discussed above in accordance with the types of metals that a MIMbase are made from. After mixing, the mixture is injected into anappropriate mold at block 404. The mold has a shape that corresponds toa base of a disc drive, such as MIM base 302 of FIG. 3. The mold isadapted to form a platform, such as MIM platform 303, and adapted toform three-dimensional features, such as MIM three-dimensional features304, that are integral with the platform.

The mold, containing the injected mixture, is heated in an oven forde-bonding at block 406. The oven is set at a temperature ofapproximately 600° C. for the de-bonding process. After de-bonding, allof the polymer bonding material will be removed or burnt and only themetal powder material is left. At block 408, the mold containing theinjected metal or combination of metals is heated in an oven forsintering. The oven is set at a temperature of approximately 1000° C.for sintering. In the sintering process, the metal powder will stick toeach other and form the solid metal base. The solid metal base, afterthe sintering process, is removed from the mold, cleaned and istherefore suitable for disc drive application. However, the solid metalbase can also be put through a machining process for re-sizing toachieve desirable dimensional tolerances and geometrical tolerances forcritical features.

It is to be understood that even though numerous characteristics andadvantages of various embodiments of the invention have been set forthin the foregoing description, together with details of the structure andfunction of various embodiments of the invention, this disclosure isillustrative only, and changes may be made in detail, especially inmatters of structure and arrangement of parts within the principles ofthe present invention to the full extent indicated by the broad generalmeaning of the terms in which the appended claims are expressed. Forexample, the particular elements may vary depending on the particularapplication for the data storage system while maintaining substantiallythe same functionality without departing from the scope and spirit ofthe present invention. In addition, although the preferred embodimentdescribed herein is directed to a base for a data storage system, itwill be appreciated by those skilled in the art that the teachings ofthe present invention can be applied to other types of structures,without departing from the scope and spirit of the present invention.

1. A data storage system comprising: an injection molded base including:a metal injection molded platform; and at least one metal injectionmolded three-dimensional feature formed integrally and simultaneouslywith the metal injection molded platform, the at least onethree-dimensional feature configured to mount data storage systemcomponents to the platform and comprising an actuator shaft protrudingfrom the metal injection molded platform.
 2. The data storage system ofclaim 1, wherein the injection molded base comprises a non-magneticmetal.
 3. The data storage system of claim 2, wherein the non-magneticmetal base comprises one of a stainless steel and an aluminum alloy. 4.The data storage system of claim 1, wherein the metal injected moldedbase comprises a magnetic metal.
 5. The data storage system of claim 4,wherein the magnetic metal base forms part of a magnetic circuit with avoice coil motor of an actuator mechanism and forms part of a magneticcircuit with a spindle motor.
 6. The data storage system of claim 4,wherein the magnetic metal comprises a soft magnetic metal.
 7. The datastorage system of claim 6, wherein the soft magnetic metal comprises oneof a permalloy, permendur, 1010 steel and iron.
 8. The data storagesystem of claim 1, wherein the at least one three dimensional featurefurther comprises one of a printed circuit board screw nut, a rampstopper and a recirculation filter support.
 9. A method comprising:obtaining an injection molded base that has a metal injection moldedplatform and a metal injection molded three-dimensional feature that isformed integrally and simultaneously with the metal injection moldedplatform, the metal injection molded three-dimensional feature comprisesa shaft protruding from the platform; and mounting a data storage systemcomponent to the three-dimensional feature, wherein the data storagesystem component comprises an actuator configured to be mounted to theshaft.
 10. The method of claim 9, wherein obtaining an injection moldedbase comprises obtaining an injection molded base including anon-magnetic metal comprising at least one of a stainless steel and analuminum alloy.
 11. The method of claim 9, wherein obtaining aninjection molded base comprises obtaining an injection molded basecomprising a magnetic metal, wherein the magnetic metal base forms partof a magnetic circuit with a voice coil motor of an actuator mechanismand forms part of a magnetic circuit with a spindle motor.
 12. A datastorage system comprising: an injection molded base including: a metalinjection molded platform; and at least one metal injection moldedthree-dimensional feature formed integrally and simultaneously with themetal injection molded platform, the at least one three-dimensionalfeature configured to mount data storage system components to theplatform and comprising a motor housing, the motor housing is recessedinto the platform from a top surface of the platform and includes acontinuous, unbroken floor.